Self-assembled Synthesis of Super-hydrophobic Polyaniline with Hierarchical Structure
Abstract
In this paper，super-hydrophobic polyaniline with hierarchical structure has been synthesized via a “soft template chemical oxidation” method with aniline as monomer，ammonium persulfate as oxidant in the solution of perfluorocaprylic acid (PFOA).The morphologies and structures of the polyaniline were further proved by SEM，FT-IR，XRD and UV-vis. When ［PFOA］ = 0.002 4 mol/L，［ANI］ = 0.022 mol/L，T =25 ℃，［APS］ = ［ANI］，the synthesized PANI was a sheet structure about tens of micrometers in length and 2~5 μm in width，in which the surface of sheet structure was composed of PANI fiber (about 1 μm in length with a diameter ca.100 nm).When ［ANI］= 0.044 mol/L，the synthesized PANI was a sheet structure of about 20 μm in length and 2~3 μm in width，in which the surface was covered with short thick irregular fibers. The water contact angles of both structures were 149° and 151°，respectively. These results demonstrate that the as-prepared PANIs exhibit excellent hydrophobic properties.
Keywords: polyaniline, super-hydrophobic, self-assembled, hierarchical structure
Full Text:
PDFReferences
WENZEL R N. Surface roughness and contact anglc[J].J Phys Chem ,1949,53 (9):1466-1467.
BAXTER S,CASSIE A В D. Wettability of porous surfaccs[J]. Trans Faraday Soc, 1944,40;546—551.
BARTHLOTT W,NEINHUIS C.Purity of the sacrcd lotus.or escapc from contamination in biological surfaces [J ]. Planta, 1997,202(l):l-8.
NEINHUIS С W.Characterization and distribution of water-re pellent, self-cleaning plant surfaces [J]. Annals of Botany, 1997,79(6): 667 — 677.
WANG Jingming, WANG Ke, JIANG Lei, et al. Effects of chemical com posit ionand nano-st ructureson the wetting behaviour of lotus leaves[j], Chemical Journal of Chinese Universities, 2010,31(8): 1596— 1599.(In Chinese)
LIU В, WANG W, JIANG G, et al. Study on hierarchical structured PDMS for surfacc supcr-hydrophobicity using imprinting with ultrafast laser structured models[J ]. Appl Surf Sci, 2016,364:528-538.
SHI Pu, CHEN Hong, GONG Huiqing, ef al. Methods to prepare superhydrophobic surface[J]. Journal of Functional Polymers , 2008,21(2) ;230 —236.
DAI Xueyu,LENG Baolin.GAO Lanling, et al. Peparation of the surfacc with superhydrophobicity[J]. Guangdong Chemical Industry,2014,41(20):90—91.(In Chinese)
BHADRA S.KHASTGIR D, SINGH N K, et al. Progress in preparation,processing and applications of polyaniline [J].ProgPolym Sci, 2009,34; 783-810.
OLEJNIK P, GNIADEK M.PALYS B. Layers of polyaniline nanotubes deposited by langmuir-blodgettmethod [J]. J Phys Chem C, 2012,116:10424 -10429.
ZHOU C, GONG A X,QU Y, et al. Hydrophobic and high adhesive polyaniline layer of rectangular microtubes fabricated by a modified intcrfacial polymerization [J ]. Appl Surf Sci, 2016, 379:124-131.
FAN H, WANG H.GUO J, et al.SDBS-assisted preparation of novel polyanilinc planar-structure; Morphology, mechanism and hydrophobicity[j]j Colloid Intcrf Sci.2011,41 1:16 — 49.
Refbacks
- There are currently no refbacks.