Study on Low Temperature Performance of Polyphosphoric Acid Modified Asphalt and Asphalt Mixture

LIU Hongying, CHANG Rui, ZHANG Mingming, ZHANG Zhenxing, НАO Peiwen

Abstract

 Through the conventional low temperature performance test and Superpave low temperature performance test, the structural performance of different polyphosphoric acid (PPA) modified asphalt binder was investigated at low temperature, and the corresponding relationship of its performance evaluation index was analyzed. Further, the anti-cracking performance of asphalt mixture at low temperature was verified by the improved trabecular bending test and TSRST, and the correlation of low temperature performance between the asphalt binder and the mixture was studied. Finally, the rationality and deficiency of the evaluation index of different low temperature performance were analyzed. The results show that PPA reduced the ductility and stiffness modulus of asphalt, and the aging had great influence on the structural performance of PPA modified asphalt at low temperature. The strain energy density index shows that PPA can improve the cracking resistance of asphalt mixture at low temperature, the anti-cracking performance of PPA compound SBR modified asphalt was better than that of SBR modified asphalt, and the freezing temperature and freeze fracture strength can more accurately evaluate the low temperature performance of PPA modified asphalt.

 

 

Keywords: road engineering,  polyphosphoric acid,  modified asphalt,  low temperature,  evaluation indexes


Full Text:

PDF


References


MAO Sanpeng. Research on polyphosphoric acid used in SBS modified asphalt [J]. Petroleum Asphalt. 2010. 24 (5): 28 — 32. (In Chinese)

ZHANG Henglong. SHI Caijun. YU Jianying. et al. Modification and its mechanism of different asphalts by polyphosphoric acid [J]. Journal of Building Materials.2013, 16( 2) : 255 — 260. (In Chinese)

FEE D. MALDONADO R. Polyphosphoric acid modification of asphalt [J]. Journal of the Transportation Research Record. 2010,2179:49-57.

WANG Yunpu. ZHANG Feng. Study on 90s road asphalt modified by polyphosphoric acid and SBR [J]. Petroleum Processing And Petrochemicals,2007.38(9) :53 — 55. (In Chinese)

YU Wenke. Study on modified asphalt with polyphosphoric acid [D]. Chongqing; College of Civil Engineering, Chongqing Jiaotong University,2011; 136 — 45. (In Chinese)

CAO Weidong, LIU Lemin. Experimental study on modified asphalt with polyphosphoric acid [J]. Journal of China Foreign Highway,2010,30(3) :252—254. (In Chinese)

FU Liqiang, WANG Ziling, HUANG Xiaoming. et al. Performance research of polyphosphoric acid modified asphalt [J]. Journal of Highway and Transportation Research and Development .2008, 5(2); 16— 19. (In Chinese)

EDWARDS Y, TASDEMIR Y. 1SACSSON U. Influence of commercial waxes and polyphosphoric acid on bitumen and asphalt concrete performance at low and medium temperatures [J]. Materials and Structures.2010,39(7) :725 — 737.

ZHANG Mingming. Study on micromechanism and performance of polyphosphoric acid modified asphalt [D]. Xi’an; Highway School, Chang’an University ,2012 :56—67. (In Chinese)

BENNERT T. MARTIN J V. Polyphosphoric acid in combination with styrene-butadiene-styrene block copolymer laboratory mixture evaluation [J]. Asphalt Paving Technology: Association of Asphalt Paving Technologists-Proceedings of the Technical Sessions, 2008,79(E-C160);773 — 791.

ZHAO Ke, DU Yuezong. Research on polyphosphoric acid modified asphalt[J]. Petroleum Asphalt, 2010,24(3) :4— 10. (In Chinese)

JTG E20 — 2011 Standard test methods of asphalt and asphalt mixtures for highway engineering [S]. Beijing: China Communications Press, 2011, 26 -30 (In Chinese)


Refbacks

  • There are currently no refbacks.